Tekanyo ea khabone ea ho robeha ha sampole e 'ngoe le e 'ngoe e sintered e fapane, ka tekanyo ea khabone ea A-2.5 awt.% mothating ona, e etsa thepa e teteaneng e batlang e se na masoba, e entsoeng ka likaroloana tsa silicon carbide tse ajoang ka ho lekana le silicon e lokolohileng. Ka keketseho ea keketseho ea khabone, tekanyo ea carbide ea silicon e sintered reaction-sintered e eketseha butle-butle, boholo ba likaroloana tsa silicon carbide boa eketseha, 'me silicon carbide e hokahane ka sebopeho sa masapo. Leha ho le joalo, tekanyo e feteletseng ea khabone e ka lebisa habonolo khaboneng e setseng 'meleng o sintered. Ha carbon black e eketsoa ho ea ho 3a, ho sintering ha sampole ha hoa fella, 'me "li-interlayers" tse ntšo li hlaha kahare.
Ha khabone e arabela le silicon e qhibilihisitsoeng, sekhahla sa katoloso ea bophahamo ba eona ke 234%, e leng se etsang hore sebopeho sa microstructure sa carbide ea silicon e sintered reaction-sintered se amane haufi-ufi le dikahare tsa carbon ka har'a billet. Ha dikahare tsa carbon ka har'a billet li le nyane, carbide ea silicon e hlahisoang ke karabelo ea silicon-carbon ha e lekane ho tlatsa masoba a potileng phofo ea carbon, e leng se fellang ka palo e kholo ea silicon e lokolohileng ka har'a sampole. Ka keketseho ea dikahare tsa carbon ka har'a billet, carbide ea silicon e sintered reaction-sintered e ka tlatsa masoba a potileng phofo ea carbon ka botlalo 'me ea hokahanya carbide ea silicon ea pele hammoho. Nakong ena, dikahare tsa silicon e lokolohileng ka har'a sampole lia fokotseha 'me bongata ba' mele o sintered boa eketseha. Leha ho le joalo, ha ho na le carbon e ngata ka har'a billet, carbide ea silicon ea bobeli e hlahisoang ke karabelo pakeng tsa carbon le silicon e potoloha toner ka potlako, e leng se etsang hore ho be thata hore silicon e qhibilihisitsoeng e kopane le toner, e leng se fellang ka carbon e setseng 'meleng o sintered.
Ho ya ka diphetho tsa XRD, sebopeho sa mokgahlelo wa sic e sintered reaction ke α-SiC, β-SiC le silicon e lokolohileng.
Nakong ea ho sintering ha karabelo ea mocheso o phahameng, liathomo tsa khabone li fallela boemong ba pele holim'a bokaholimo ba SiC β-SiC ka ho thehoa ha silicon e qhibilihisitsoeng ea α-secondary. Kaha karabelo ea silicon-carbon ke karabelo e tloaelehileng ea exothermic e nang le mocheso o mongata oa karabelo, ho phola ka potlako kamora nako e khuts'oane ea karabelo ea mocheso o phahameng e sa reroang ho eketsa ho ts'oaroa ha khabone e qhibilihisitsoeng ka har'a silicon e metsi, e le hore likaroloana tsa β-SiC li hlahe ka mokhoa oa khabone, ka hona li ntlafatsa litšobotsi tsa mechini tsa thepa. Ka hona, ntlafatso ea lijo-thollo tsa β-SiC ea bobeli e molemo ntlafatsong ea matla a kobehang. Sistiming ea motsoako oa Si-SiC, litaba tsa silicon e lokolohileng thepa lia fokotseha ha litaba tsa khabone li eketseha ka lebaka la keketseho ea litaba tsa khabone thepa e tala.
Qetello:
(1) Viscosity ea slurry e lokisitsoeng ea ho lahla e eketseha ha bongata ba carbon black bo eketseha; Boleng ba pH ke alkaline 'me butle-butle boa eketseha.
(2) Ka keketseho ea dikahare tsa khabone 'meleng, boima le matla a ho kobeha a liseramike tse sintered reaction-sinter tse lokisitsoeng ka mokhoa oa ho tobetsa li ile tsa qala ho eketseha ebe lia fokotseha. Ha bongata ba khabone e ntšo bo le makhetlo a 2.5 ho feta bongata ba pele, matla a ho kobeha a lintlha tse tharo le boima ba billet e tala kamora ho sintering ha reaction li phahame haholo, e leng 227.5mpa le 3.093g/cm3, ka ho latellana.
(3) Ha 'mele o nang le khabone e ngata haholo o siloa, mapetso le libaka tse ntšo tsa "sandwich" li tla hlaha 'meleng oa' mele. Lebaka la ho petsoha ke hore khase ea silicon oxide e hlahisoang nakong ea ho siloa ha karabelo ha e bonolo ho e ntša, e bokellana butle-butle, khatello ea phahama, 'me phello ea eona ea ho jaha e lebisa ho petsoheng ha billet. Sebakeng sa "sandwich" se setšo ka hare ho sinter, ho na le khabone e ngata e sa ameheng karabelong.
Nako ea poso: Phupu-10-2023