I-carbon-carbon sagger/treyi yenziwe ngezinto ezidityanisiweyo zekhabhoni (CFC) ezisetyenziswa kwisikhongozeli esinobushushu obuphezulu, inobunzima obuphantsi, amandla aphezulu, ukumelana nokutsha kobushushu obuhle, ubunyulu obuphezulu, ukumelana nokuguguleka kunye nokusebenza okugqwesileyo, sisixhobo esishushu esikumgangatho ophezulu, usetyenziso luquka: izixhobo ze-anode zebhetri ye-lithium, isitya se-lithium iron phosphate anode, isikhephe se-powder metallurgy esinobushushu obuphezulu kunye nokunye.
I-VET Energy igxile kwizinto ezenziwe ngokwezifiso ze-carbon-carbon composite (CFC) ezisebenzayo kakhulu, sinikezela ngezisombululo ezipheleleyo ukusuka ekuqulunqweni kwezinto ukuya ekuvelisweni kweemveliso ezigqityiweyo. Ngenxa yezakhono ezipheleleyo ekulungiseleleni i-carbon fiber preform, ukufakwa komphunga weekhemikhali, kunye nomatshini wokuchwetheza ngokuchanekileyo, iimveliso zethu zisetyenziswa kakhulu kwizicelo ze-semiconductor, photovoltaic, kunye ne-high-temperature indasitiri.
| Idatha yoBugcisa yeKhabhoni-I-Carbon Composite | ||
| Isalathiso | Iyunithi | Ixabiso |
| Unizi lolwapho kuyiwa khona | g/cm3 | 1.40~1.50 |
| Umxholo wekhabhoni | % | ≥98.5~99.9 |
| Uthuthu | I-PPM | ≤65 |
| Ukuqhuba kwe-thermal (1150℃) | W/mk | 10~30 |
| Tensile strength | I-Mpa | 90~130 |
| Amandla okuGuquka | I-Mpa | 100~150 |
| Amandla oxinzelelo | I-Mpa | 130~170 |
| Amandla okucheba | I-Mpa | 50~60 |
| Amandla okuGxotha aphakathi kwe-Interlaminar | I-Mpa | ≥13 |
| Ukumelana nombane | Ω.mm2/m | 30~43 |
| I-Coefficient yoKwandiswa koBushushu | 106/K | 0.3~1.2 |
| Ubushushu bokucubungula | ℃ | ≥2400℃ |
| Umgangatho womkhosi, ukufakwa kwesithando somlilo esipheleleyo sekhemikhali, ukuluka inaliti ye-3D eyenziwe yiToray carbon fiber T700 engeniswe ngaphandle. Iinkcukacha zezinto: ububanzi obuphezulu bangaphandle yi-2000mm, ubukhulu bodonga yi-8-25mm, ukuphakama yi-1600mm | ||