I-Carbon-carbon sagger/ithreyi yenziwe nge-carbon carbon composite material(CFC) icutshungulwa ibe yisitsha esinezinga lokushisa eliphezulu, inesisindo esilula, amandla aphezulu, ukumelana nokushaqeka okuhle kokushisayo, ukuhlanzeka okuphezulu, ukumelana nokugqokwa kanye nochungechunge lokusebenza okuhle kakhulu, iyinto enhle kakhulu eshisa kakhulu emazingeni okushisa aphezulu, izinhlelo zokusebenza zifaka: izinto ze-lithium battery anode, isitsha se-lithium iron phosphate, i-boluat metal sinteratureing metal sinterature, i-boluat sinterature ye-boluat sinterature.
I-VET Energy ikhethekile ezintweni ezenziwe ngokwezifiso ze-carbon-carbon-carbon composite (CFC), sihlinzeka ngezixazululo eziphelele kusukela ekwakhiweni kwezinto ezibonakalayo kuya ekukhiqizeni imikhiqizo eqediwe. Ngamakhono aphelele ekulungiseleleni i-carbon fibre preform, i-chemical vapor deposition, kanye nomshini wokunemba, imikhiqizo yethu isetshenziswa kabanzi ku-semiconductor, i-photovoltaic, kanye nezicelo zesithando somlilo sezimboni ezinezinga eliphezulu lokushisa.
| Idatha Yezobuchwepheshe Yekhabhoni-Ikhabhoni Composite | ||
| Inkomba | Iyunithi | Inani |
| Ukuminyana ngobuningi | g/cm3 | 1.40~1.50 |
| Okuqukethwe kwekhabhoni | % | ≥98.5~99.9 |
| Umlotha | I-PPM | ≤65 |
| I-Thermal conductivity (1150 ℃) | W/mk | 10-30 |
| Amandla aqinile | Mpa | 90-130 |
| Amandla e-Flexural | Mpa | 100 ~ 150 |
| Amandla acindezelayo | Mpa | 130-170 |
| Amandla okugunda | Mpa | 50-60 |
| Amandla e-Interlaminar Shear | Mpa | ≥13 |
| Ukumelana nogesi | Ω.mm2/m | 30-43 |
| I-Coefficient of Thermal Expansion | 106/K | 0.3~1.2 |
| Icubungula izinga lokushisa | ℃ | ≥2400℃ |
| Ikhwalithi yezempi, ukufakwa kwesithando somlilo samakhemikhali esigcwele umhwamuko, ukunitha kwenaliti ye-3D eyenziwe ngaphandle kwe-Toray carbon fiber T700 eyalukwe ngaphambili. Ukucaciswa kwezinto ezibonakalayo: ububanzi bangaphandle obukhulu 2000mm, ukujiya kodonga 8-25mm, ukuphakama 1600mm | ||