Babban fasali na hita graphite:
1. daidaiton tsarin dumama.
2. ingantaccen amfani da wutar lantarki da kuma yawan nauyin wutar lantarki.
3. juriya ga tsatsa.
4. rashin iskar oxygen.
5. tsarkin sinadarai mai yawa.
6. ƙarfin injina mai girma.
Amfanin shine ingantaccen makamashi, ƙima mai yawa da kuma ƙarancin kulawa. Za mu iya samar da graphite crucible, graphite mold da dukkan sassan hita graphite.
Babban sigogi na hita graphite
| Bayanin Fasaha | Semicera-M3 |
| Yawan Yawa (g/cm3) | ≥1.85 |
| Abubuwan da ke cikin Toka (PPM) | ≤500 |
| Taurin bakin teku | ≥45 |
| Takamaiman Juriya (μ.Ω.m) | ≤12 |
| Ƙarfin Lankwasawa (Mpa) | ≥40 |
| Ƙarfin Matsi (Mpa) | ≥70 |
| Matsakaicin Girman Hatsi (μm) | ≤43 |
| Ma'aunin Faɗaɗawar Zafi Mm/°C | ≤4.4*10-6 |
Makamashin VET shine Lallaiainihin masana'anta na samfuran graphite da silicon carbide na musamman tare da murfin CVD,iya bayarwadaban-dabansassa na musamman don masana'antar semiconductor da photovoltaic. OƘungiyar fasaha ta ku ta fito ne daga manyan cibiyoyin bincike na cikin gida, za su iya samar da ƙarin mafita na kayan aiki na ƙwararruna ka.
Muna ci gaba da haɓaka hanyoyin ci gaba don samar da ƙarin kayan aiki masu inganci,kumasun yi amfani da wata fasaha ta musamman da aka yi wa rijista, wadda za ta iya sa haɗin da ke tsakanin murfin da substrate ya yi ƙarfi kuma ya zama ba shi da sauƙin rabuwa.
Fsamfuranmu masu zuwa:
1. Juriyar iskar shaka mai zafi har zuwa 1700℃.
2. Tsarkakakken tsarki da kumadaidaiton zafi
3. Kyakkyawan juriya ga tsatsa: acid, alkali, gishiri da kuma sinadaran halitta.
4. Babban tauri, ƙaramin surface, ƙananan barbashi.
5. Tsawon rai da kuma tsawon rai
| CVD SiC薄膜基本物理性能 Abubuwan asali na zahiri na CVD SiCshafi | |
| 性质 / Kadara | 典型数值 / Darajar da Aka Saba |
| 晶体结构 / Tsarin Crystal | Matakin FCC β多晶，主要为（111) 取向 |
| 密度 / Yawan yawa | 3.21 g/cm³ |
| 硬度 / Tauri | 2500 维氏硬度 (500g kaya) |
| 晶粒大小 / Size na hatsi | 2 ~ 10μm |
| 纯度 / Tsarkakewar Sinadarai | 99.99995% |
| 热容 / Ƙarfin Zafi | 640 J·kg-1·K-1 |
| 升华温度 / Zafin Sublimation | 2700℃ |
| 抗弯强度 / Ƙarfin Lankwasawa | 415 MPa RT maki 4 |
| 杨氏模量 / Matashin Young | 430 GPA lanƙwasa 4pt, 1300℃ |
| 导热系数 / ThermalGudanar da wutar lantarki | 300W·m-1·K-1 |
| 热膨胀系数 / Faɗaɗawar Zafi (CTE) | 4.5×10-6K-1 |