Izinto ezidityanisiweyo zekhabhoni/khabhoni ziye zaba sisizukulwana esitsha sezinto ezidityanisiweyo ezithatha indawo yezinto ezidityanisiweyo ezisekwe kwisinyithi ngenxa yeempawu zazo ezikhethekileyo zoomatshini, ubushushu kunye nokungqubana kunye nokuguguleka.
Iimpawu zayo eziphambili zezi zilandelayo:
(1) Uxinano lwezinto luphantsi njenge-1.5g/cm3, nto leyo enokunciphisa kakhulu ubunzima besakhiwo sediski yebrake;
(2) Le nto inokumelana nokuguguleka okuhle kakhulu kwaye idiski yebrake inobomi obude benkonzo, obuphindwe kabini kunezixhobo ze-metal matrix composite;
(3) I-Stable dynamic friction factor, iipropati ezilungileyo zokulwa nokunamathela kunye nokunamathela;
(4) Yenza lula uyilo lwediski yebrake kwaye akufuneki zizinto ezongezelelweyo zokungqubana, izihlanganisi, amathambo ebrake, njl.njl.;
(5) I-coefficient encinci yokwandisa ubushushu, umthamo ophezulu wobushushu (ophindwe kabini kune-iron), kunye nokuqhuba okuphezulu kobushushu;
(6) Idiski yebrake yekhabhoni/khabhoni inobushushu obuphezulu bokusebenza kunye nokumelana nobushushu ukuya kuthi ga kwi-2700℃.
Idatha yoBugcisa yeKhabhoni-I-Carbon Composite | ||
| Isalathiso | Iyunithi | Ixabiso |
| Unizi lolwapho kuyiwa khona | g/cm3 | 1.40~1.50 |
| Umxholo wekhabhoni | % | ≥98.5~99.9 |
| Uthuthu | I-PPM | ≤65 |
| Ukuqhuba kwe-thermal (1150℃) | W/mk | 10~30 |
| Tensile strength | I-Mpa | 90~130 |
| Amandla okuGuquka | I-Mpa | 100~150 |
| Amandla oxinzelelo | I-Mpa | 130~170 |
| Amandla okucheba | I-Mpa | 50~60 |
| Amandla okuGxotha aphakathi kwe-Interlaminar | I-Mpa | ≥13 |
| Ukumelana nombane | Ω.mm2/m | 30~43 |
| I-Coefficient yoKwandiswa koBushushu | 106/K | 0.3~1.2 |
| Ubushushu bokucubungula | ℃ | ≥2400℃ |
| Umgangatho womkhosi, ukufakwa kwesithando somlilo esipheleleyo sekhemikhali, ukuluka inaliti ye-3D eyenziwe yiToray carbon fiber T700 engeniswe ngaphandle. Iinkcukacha zezinto: ububanzi obuphezulu bangaphandle yi-2000mm, ubukhulu bodonga yi-8-25mm, ukuphakama yi-1600mm | ||