SiC Coated Barrel Susceptor

Kufotokozera Kwachidule:

VET Energy SiC Coated Barrel Susceptor ndi chinthu chogwira ntchito bwino kwambiri chomwe chimapangidwa kuti chipereke magwiridwe antchito okhazikika komanso odalirika kwa nthawi yayitali. Chimalimbana bwino ndi kutentha komanso kutentha kofanana, kuyera kwambiri, komanso kukana kukokoloka kwa nthaka, zomwe zimapangitsa kuti chikhale yankho labwino kwambiri pakugwiritsa ntchito ma wafer.

Malo Ochokera:China

Kapangidwe ka Crystal:Gawo la FCCβ

Kuchulukana:3.21 g/cm;

Kuuma:2500 Vickers;

Kukula kwa Tirigu:2 ~ 10μm;

Kuyera kwa Mankhwala:99.99995%;

Kutha Kutentha:640J·kg-1·K-1;

Kutentha kwa Sublimation:2700℃;

Mphamvu ya Feleksiyumu:415 Mpa (RT 4-Point);

Modulus ya Young:430 Gpa (kupindika kwa 4pt, 1300℃);

Kukula kwa Kutentha (CTE):4.5 10-6K-1;

Kutentha kwa Matenthedwe:300（W/MK）;

Tumizani imelo kwa ife Tsitsani ngati PDF

Tsatanetsatane wa Zamalonda

Ma tag a Zamalonda

Chotsukira mbiya is a kiyigawo lomwe limagwiritsidwa ntchito popanga zinthu zosiyanasiyana za semiconductor.Timagwiritsa ntchito ukadaulo wathu wokhala ndi patent kuti tipangechotsukira mbiyandichiyero chapamwamba kwambiri,zabwinochophimbakufananandi moyo wabwino kwambiri wautumiki, komansokukana kwambiri mankhwala ndi mphamvu zokhazikika pa kutentha.

VET Energy ndi awopanga weniweni wa zinthu zopangidwa ndi graphite ndi silicon carbide zokhala ndi zokutira za CVD,akhoza kuperekazosiyanasiyanazida zopangidwira makampani opanga ma semiconductor ndi photovoltaic. OGulu lanu laukadaulo limachokera ku mabungwe apamwamba ofufuza zamkati, likhoza kupereka mayankho aukadaulo ambirizanu.

Timapanga njira zamakono nthawi zonse kuti tipereke zipangizo zamakono kwambiri,ndiagwiritsa ntchito ukadaulo wapadera wokhala ndi patent, womwe ungapangitse kuti mgwirizano pakati pa chophimba ndi substrate ukhale wolimba komanso wosasinthasintha.

FZakudya za zinthu zathu:

1. Kukana kutentha kwambiri kwa okosijeni mpaka 1700℃.
2. Kuyera kwambiri ndikufanana kwa kutentha
3. Kukana dzimbiri bwino: asidi, alkali, mchere ndi zinthu zachilengedwe.
4. Kulimba kwambiri, pamwamba pang'ono, tinthu tating'onoting'ono.
5. Moyo wautali komanso wokhalitsa

Matenda a mtima (CVD) SiC薄膜基本物理性能 Makhalidwe oyambira a CVD SiCchophimba
性质 / Katundu	典型数值 Mtengo Wamba
晶体结构 / Kapangidwe ka Crystal	Gawo la FCC β多晶，主要為（111）取向
密度 / Kuchulukana	3.21 g/cm³
硬度 / Kuuma	2500 维氏硬度 (500g katundu)
晶粒大小 / Tirigu Waukulu	2 ~ 10μm
纯度 / Kuyera kwa Mankhwala	99.99995%
热容 / Kutha Kutentha	640 J·kg^-1·K^-1
升华温度 / Kutentha kwa Sublimation	2700℃
抗弯强度 / Mphamvu Yosinthasintha	415 MPa RT 4-point
杨氏模量 / Young's Modulus	430 Gpa 4pt kupindika, 1300℃
导热系数 / KutenthalKuyendetsa bwino	300W·m^-1·K^-1
热膨胀系数 / Kukulitsa Kutentha (CTE)	4.5×10^-6K^-1