Mofuta, tshebetso le tshebediso ya elektrode
Mofuta oa li-electrode
Li-electrode tsa carbonaceous li ka aroloa ka li-electrode tsa carbon, li-electrode tsa graphite le li-electrode tse ipakelang ho latela ts'ebeliso ea tsona le lits'ebetso tsa tlhahiso.
Electrode ea khabone e entsoe ka anthracite ea molora o tlaase, coke ea metallurgical, coke ea pitch le coke ea petroleum. E entsoe ka tekanyo e itseng le boholo ba likaroloana. Ha e eketsoa, asphalt ea binder le tar lia kopanngoa, 'me motsoako o hlohlelletsoa ka ho lekana mochesong o loketseng. E thehoa, 'me qetellong e calcining butle-butle ka har'a roaster. E ka aroloa ka li-electrode tsa tlhaho tsa graphite, li-electrode tsa maiketsetso tsa graphite, li-electrode tsa khabone le li-electrode tse khethehileng tsa khabone.
Electrode ea graphite (graphiteelectrode) e entsoe ka petroleum coke le pitch coke e le thepa e tala, ebe e kenngoa ka ontong ea motlakase e hanyetsanang le graphitized ka mocheso oa 2273 ~ 2773K, 'me e etsoa electrode ea graphite ka graphitization. Electrode ea graphite e arotsoe hape ka Mofuta o latelang.
Electrode e tloaelehileng ea grafiti e lumella tšebeliso ea li-electrode tsa grafiti tse nang le boima ba hona joale bo ka tlase ho 17 A/cm2, 'me e sebelisoa haholo bakeng sa lionto tse tloaelehileng tsa motlakase tse kang ho etsa tšepe, ho hloekisa silicon le phosphorus e mosehla.
Bokaholimo ba electrode ea graphite e koahetsoeng ka anti-oxidation bo koahetsoe ka lera le sireletsang (graphite electrode antioxidant) e tsamaisang motlakase le e hanelang oxidation ea mocheso o phahameng, e fokotsang tšebeliso ea electrode nakong ea ho etsa tšepe (19% ~ 50%) le ho lelefatsa bophelo ba tšebeletso ea electrode (22% ~ 60%), e fokotsang tšebeliso ea matla ea electrode.
Electrode ea graphite e matla haholo e lumella tšebeliso ea li-electrode tsa graphite tse nang le boima ba hona joale ba 18 ho isa ho 25 A/cm2, e sebelisoang haholo-holo liontong tsa arc tsa motlakase tse matla haholo bakeng sa ho etsa tšepe.
Li-electrode tsa grafiti tse nang le matla a phahameng haholo li lumella tšebeliso ea li-electrode tsa grafiti tse nang le matla a hona joale a fetang 25 A/cm2. Haholo-holo li sebelisoa lifonong tsa arc tsa motlakase tse etsang tšepe tse nang le matla a phahameng haholo.
Electrode e iketsang (selfbakingelectrode) e sebedisa anthracite, coke, le bitumen le tar e le thepa e tala, e etsa peista ya electrode mochesong o itseng, ebe e kenya peista ya electrode ka hara khetla ya electrode e kentsweng seboping sa motlakase (jwalo ka ha ho bontshitswe ho Setshwantsho sa 1), Mokgweng wa tlhahiso ya seboping sa motlakase, mocheso wa Joule o hlahiswang ke ho feta ha motlakase le mocheso o tsamaisang ka seboping di a iketsa mme di apehilwe. Electrode e jwalo e ka sebediswa ka ho tswela pele, mme e ka thehwa ka ho kopanya lehlakore le lelelele mme e ka tjheswa ka bophara bo boholo. Electrode e iketsang e sebediswa haholo bakeng sa tlhahiso ya ferroalloy ka lebaka la tshebetso ya yona e bonolo le theko e tlase.
Setšoantšo sa 1 Setšoantšo sa khetla ea elektrode
Khetla ea electrode e le 'ngoe; sekhechana sa likhopo tse peli; leleme la khutlotharo tse tharo
Tshebetso e ka sehloohong ea botekgeniki ea electrode
Thepa ea electrode e lokela ho ba le litšobotsi tse latelang tsa fisiks:
Ho tsamaisa motlakase ho betere, ho hanyetsa ho honyenyane, ho fokotsa tahlehelo ea matla a motlakase, ho fokotsa ho theoha ha motlakase oa letlooa le lekhutšoanyane, le ho eketsa motlakase o sebetsang ho eketsa matla a letamo le qhibilihisitsoeng;
Sebaka sa ho qhibiliha se phahame;
Koefficient ea katoloso ea mocheso e nyane, ha mocheso o fetoha ka potlako, ha ho bonolo ho holofala, 'me khatello ea ka hare e bakoang ke phetoho ea mocheso e ke ke ea hlahisa mapetso a manyane ho eketsa khanyetso;
E na le matla a lekaneng a mechini mochesong o phahameng;
Litšila li tlase 'me litšila ha li silafatse monko o nkhang hamonate.
Litšobotsi tsa bohlokoa tsa tekheniki tsa electrode ea khabone, electrode ea graphite le electrode e ipakelang li bontšitsoe ho Tafole ea 1 le Litšoantšo tsa 2 le tsa 3.
Tafole ea 1 Tshebetso ea botekgeniki ea li-electrode
Setšoantšo sa 2 Phetoho ea ho hanyetsa ha electrode ea khabone le electrode ea graphite ka mocheso
Setšoantšo sa 3 Ho tsamaisoa ha mocheso oa li-electrode tsa khabone le graphite e le mosebetsi oa mocheso
Khetho ea li-electrode indastering ea ferroalloy
Li-electrode tse ipakelang li sebelisoa haholo ho qhibilihiseng tšepe, ho hloekisa ferrosilicon, motsoako oa silicon chromium, motsoako oa silicon ea manganese, ferromanganese e nang le khabone e ngata, ferrochrome e nang le khabone e mahareng le e tlase, ferromanganese e nang le khabone e mahareng le e tlase, ferrochrome e nang le khabone e mahareng le e tlase, motsoako oa silicon calcium, tšepe ea tungsten. Li-electrode tse ipakelang li atisa ho eketsa tlhahiso ea li-alloy, mabanta a tšepe ho ba carbon, 'me li hlahisa li-alloy tsa tšepe le litšepe tse hloekileng tse nang le khabone e tlase haholo. Haeba carbon ferrochrome, tšepe ea silicon ea indasteri le manganese, li-electrode tsa carbon kapa graphite li lokela ho sebelisoa.
电极的种类、性能及其用途
电极种类
碳质电极按其用途及制作工艺不同可分為碳素电极、石墨电极和自焙电极三种.
碳素电极(carbonelectrode)是以低灰分的无烟煤、冶金焦、沥青焦和石油焦為原料，按一定的比例和粒度组成.混合时加入黏结剂沥.青和焦油，在适当的温度下搅拌均匀后压制成形，最后在焙烧炉缓慢焙烧制得。可分为天然石墨电极、人造石墨电极、碳电极以及特种碳素电极四类。
石墨电极(graphiteelectrode)以石油焦和沥青焦為原料制成碳素电极，再放到温度為2273〜2773K的石墨化电阻炉中，经石墨化而制成石墨电极„石墨电极又分为以下几。
普通功率石墨电极允许使用电流密度低于17A/cm2的石墨电极，主要用于炼钢、炼硅、炼黄磷等的普通功率电炉.
抗氧化涂层石墨电极表面涂覆既能导电又耐高温氧化的保护层(石墨电极抗氧化剂)，降低炼钢时的电极消耗(19%〜50%),延长电极的使用寿命(22%〜60%),降低电极的电能消耗。
高功率石墨电极允许使用电流密度為18〜25A/cm2的石墨电极，主要用于炼钢的高功率电。
超高功率石墨电极允许使用电流密度大于25A/cm2的石墨电极。主要用于超高功率炼钢。
自焙电极(selfbakingelectrode)用无烟煤、焦炭以及沥青和焦油为原料，在一定温度下制成电极糊，然后把电极糊装入已安装在电炉上的电极壳中(如图1所示)，在电炉上的电极壳中(如图1所示)中依靠电流通过时所产生的焦耳热和炉内传导热，自行烧结焦化。边给结成形，且可焙烧成大直径的。自焙电极不仅工艺简单，成本也低，因
图1 电极壳示意图
1-电极壳;2-筋片;3-三角形舌片
电极的主要技术性能
电极材料应具有下列物理化学特性:
导电性要好，电阻率要小，以减少电能的损失，减少短网压降，提高有效电压，以提高熔，以提高熔;
熔点要高;
热膨胀系数要小，当温度急变时，不易变形，不能因温度变化带來的内应力产生细小的蔡小的内应力产生绂小的蔚小的蔚小;
高温下要有足够的机械强度;
杂质要低，而且杂质不污染所冶炼的品种。
碳素电极、石墨电极和自焙电极的主要技术性能如表1和图2、图3所示.
表1 电极技术性能
图2 碳素电极和石墨电极电阻率随温度的变化情况
图3 碳素电极和石墨电极热导率随温度的变化情况
铁合金工业中电极的选用
自焙电极广泛用于铁合金冶炼，炼制硅铁、硅铬合金、锰硅合金、高碳锰铁、高碳铬铁、中低碳锰铁、中低碳铬铁、硅钙合金、钨铁等。自焙电极易使生产合金增碳，铁皮带入碳，生产含碳很低的铁合金和纯金属，如果碳铬铁、工业硅和金属锰应采用碳素电极或石墨电极。